Tire balancing

ABSTRACT

A method and composition of matter for balancing tire and rim assemblies of vehicles is disclosed wherein the composition of matter has rounded balancing elements of different sizes to line the interior of a tire casing and to move over the lining to offset points of imbalance.

BACKGROUND OF THE INVENTION

This invention relates to an improvement in a method of balancing tires using a free flowing material within a tire casing and in the composition of said material.

Most tire and rim assemblies require balancing to prevent vibration within the vehicle while it is in motion. One currently popular, method of balancing tire and rim assemblies involves rotation of the assembly on a computerized balancing machine to determine the location and size of weights necessary to obtain balanced rotation. Lead weights of the determined size are then clamped to the assembly at the indicated points to complete the balancing procedure. There are other similar "fixed weight" systems known for tire balancing. Some disadvantages of this type of system are that tire balancing equipment is expensive, tire balancing requires a skilled operator and is time consuming, and tires must be rebalanced at regular intervals due to effects of varying tread wear.

Continuous self balancing systems overcome many of the disadvantages of the above fixed weight systems. Continuous self balancing systems use the principle that free flowing materials contained in a vessel in rotation will seek a distribution in balance about the centre of rotation and will tend to offset, by mass damping, any imbalance inherent in the vessel. The effectiveness of a dynamic balancing system is dependent in part on the ease with which balancing material can move within the vessel to positions which offset points of imbalance.

In one application of this principle an annular ring is placed circumferentially about a rim and partially filled with heavy materials that will flow under the influence of centrifugal force. One such balancer uses mobile weights such as ball bearings which are free to roll to any point on the ring. The effectiveness of this method is limited by the roundness of the ball bearings, the concentricity of the ring to the geometric axis and the inherent rolling resistance of the balls in the ring.

Liquids have been attempted in self balancing systems to improve the mobility of the balancing material. U.S. Pat. No. 2,687,918 to Bell discloses an annular tube attached to a tire rim partially filled with mercury for continuous balancing of the tire and rim assembly. Several disadvantages exist for this method, the principal ones being high cost and toxicity of mercury, the difficulty of ensuring concentricity of the annular tube and the need for special rims.

The use of free flowing powdered materials in balancing compensators was taught in U.S. Pat. No. 4,109,549, in which an annular tube was filled with other dense materials such as powdered tungsten.

A different means for applying the self balancing principle was disclosed in U.S. Pat. No. 5,073,217 to Fogal. A free flowing balancing powder was placed directly within a pneumatic tire, instead of within a concentric annular tube. Pulverent polymeric/copolymeric synthetic plastic material in the range of 8-12 screen size and 40-200 screen size were disclosed. The patent taught that the powder within the fire would distribute within the tire under centrifugal forces to dampen vibration. Placing the balancing media within the tire has two primary advantages. The balancing force is positioned close to the point of imbalance and extraneous annular rings are not required. The disadvantage of Fogal is that powdered products produced from a grinder or pulverizer tend to have particles with an irregular shape which increases resistance or friction to fluidity. It is unlikely that heavy liquids, such as mercury, could be substituted advantageously in Fogal's application, however, both because of above mentioned safety reasons and because such liquids may be incompatible with or corrosive to the composition of a tire.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a method of tire balancing using an improved solid particulate material within a tire casing to obtain better fluidity for more efficient balancing of a tire and rim assembly.

The present invention uses the known principle of balancing through mass damping and the known method of using a solid materials within a pneumatic tire to obtain a dynamic balance while the wheel is in rotation. The improvement of this invention lies primarily in the composition of the mixture of the balancing material. The mixture comprises first beads which are small, dense beads and second beads which are larger, less dense beads. Beads of a substantially rounded shaped reduce friction and improve the mobility of the material during balancing.

The small, dense beads may be formed of atomized metallic particles which form during atomization as tiny balls. Corrosion resistant metal such as bronze, brass, zinc, tin, copper, stainless steel, nickel or silver or alloys of same may be used. Selection may be made after consideration of factors such as cost, availability and suitability for forming into small rounded shapes. In preferred embodiments the metallic component is selected from bronze, brass or zinc and atomized to form tiny balls, hereafter called "micro-spheres". The micro-spheres have round surfaces which permit them to roll over each other with less friction than sharp edged particles. The metallic micro-spheres have the greatest density (about 5-9 gr/cm³) of the materials in the mixture so that they are urged to the outside of the other materials during rotation. The small size of the micro-spheres enables them to filter through the other materials during rotation. The interior circumference of a tire is usually riddled with small pockets and ridges produced during the tire moulding process. These surface defects cause erratic movement of the balancing media and reduce its effectiveness. During rotation the micro-spheres are forced against the tire casing to fill in imperfections or voids on the tire wall to form a smooth lining which allows the remaining balancing media to move about the tire casing with less impediment. The excess of the micro-spheres, after voids and ridges are levelled, act as part of the balancing material and move to offset points of imbalance.

The larger, less dense beads are also rounded and may be formed from glass, ceramics, alumina, corderite, porcelain or titanates. These beads function as the primary balancing material and form the largest portion by weight of the mixture. Glass spheres or beads of density 2-3 gr/cm³ are preferred. The glass beads are larger but less dense than the metallic micro-spheres. Thus the glass beads tend to ride over the metallic micro-spheres to move easily to points of imbalance to dampen vibrational energy. The glass beads are more durable than thermoplastic particles of Fogal and less prone to degradation.

The mixture may also include a partitioning agent, such as vermiculite having a specific gravity in the range 2-3 gr/cm³ , mica or other monoclinic non-reactive crystalline minerals, to separate and lubricate the mixture to enable all components of the mixture to maintain free-flowing characteristics. Vermiculite is preferred.

A suitable desiccant, such as silica gel, Al₂ O₃, CaCl₂ or CaSO₄ may be added to the mixture to prevent agglomeration in the presence of moisture. Silica Gel is preferred as a desiccant to maintain a dry atmosphere in the tire casing. The small particles used in this type of balancing system tend to be hydroscopic and may agglomerate in the presence of moisture. Agglomerated particles will cause a dramatic reduction in balancing efficiency. The silica gel tends to ameliorate this condition.

A preferred mixture of this invention is as follows.

    ______________________________________                                         MATERIAL       SIZE       CONCENTRATION                                        ______________________________________                                         Non-ferrous atomized metal                                                                    80-325 mesh                                                                               10-30%                                               (e.g., bronze or brass)                                                        Glass beads     20-40 mesh                                                                               40-85%                                               (Lead free - soda lime type)                                                   Vermiculite    20-325 mesh                                                                               10-30%                                               Silica Gel      20-40 mesh                                                                               2-5%                                                 ______________________________________                                    

It has been found that this invention will work effectively with any conventional multi-wheel vehicle tire and rim assembly. It will be appreciated, however, that the amount of material to balance a particular assembly will vary in quantity and proportion, according to the type of assembly and the size of the tire and rim assembly. Correct amounts and proportions may be determined empirically by persons skilled having the benefit of this disclosure and the current state of the art. To illustrate in general terms, a steering tire of a truck (11×24.5) may require about 400 grams while a truck driving tire may require 500 grams of the mixture. Automobile tires may require only 160 grams of the mixture but are much more sensitive to vibration than truck tires and therefore require more vehicle specific and careful measuring.

BRIEF DESCRIPTION OF THE DRAWINGS

In the figures which illustrate a preferred embodiment of this invention;

FIG. 1 is an illustration of a tire and rim assembly cut away to show the interior of the tire casing having the balancing material of this invention,

FIG. 2 is an illustration of a cross section of a tire and rim assembly showing the balancing material of this invention, and

FIG. 3 is a side sectional view of a tire showing the distribution of the mixture of this invention.

DETAILED DESCRIPTION OF THE DRAWINGS

In the figures illustrating this invention like numerals indicate like elements.

In FIG. 1, a tire (1) is shown mounted on a rim (2) which, in turn, is mounted on an axle (3) of a vehicle (4). The interior of the tire casing (5) is ordinarily filled with air. The balancing material (6) of this invention lies about the periphery of the tire casing (5) while the wheel is in rotation by reason of the centrifugal force exerted on the material (6).

As illustrated in FIG. 2, the interior of the tire casing (5) has many voids and surface irregularities (7) (which are accentuated in the illustration).

The atomized metal micro-spheres (8) are shown to lie in and about the surface irregularities (7) of the tire casing (5). The micro-spheres (8) fill the voids and surface irregularities (7) and form a smooth, slippery surface for movement of the remainder of the balancing material. The excess of the micro-spheres acts as balancing material. Glass beads (9) roll over the micro-spheres (8) and act as the primary balancing material. Vermiculite (not shown) and silica gel (not shown) are interspersed in the material to act as a lubricant and a desiccant, respectively.

The preferred proportions of the balancing mixture for use in truck tires is as follows:

    ______________________________________                                                atomized metal                                                                          17%                                                                   glass beads                                                                             70%                                                                   vermiculite                                                                             10%                                                                   silica gel                                                                               3%                                                            ______________________________________                                    

For automobile tires, the preferred mixture is:

    ______________________________________                                                micro-spheres                                                                           24%                                                                   glass beads                                                                             65%                                                                   vermiculite                                                                              9%                                                                   silica gel                                                                               2%                                                            ______________________________________                                    

In operation, the balancing mixture may be poured into a new tire casing as it is assembled onto a rim. In tire rim assemblies previously constructed, the sealing bead about the rim may be broken and the mixture poured into the tire casing. Alternatively the mixture may be poured into the valve stem or mixed with the air which pressurizes the fire. Once a tire on a vehicle begins to rotate, the balancing material (6) distributes itself within the tire casing (5). As the speed of rotation increases, the metallic micro-spheres (8) tend to filter to the outside adjacent the tire casing and to fill the voids and surface irregularities (7), thereby forming a smooth inner surface. The lighter and larger glass spheres (9) then roll over the micro-spheres to adjust to a position opposite a point of imbalance (10).

As illustrated in FIG. 3, the material (6) distributes within the tire casing (5) so that a thicker portion of the material (6) lies opposite the point of imbalance (10), while some of the balancing material (6) is distributed about the entire inner surface of the tire casing (5). The distribution of the balancing material (6) acts as mass damping to overcome the eccentric force which would otherwise be introduced by the point of imbalance (10), so that the tire (1) turns smoothly. 

The invention claimed is:
 1. A mixture for balancing a tire comprising; a first portion in a range of 15% to 30% by weight of the mixture of first beads of atomized metallic particles having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 70% to 85% by weight of the mixture of second beads selected from the group consisting of glass, ceramics, alumina, corderite, porcelain and titanates having a specific gravity in the range of 2-5 and a mesh size in the range of 20-40.
 2. A mixture for balancing a tire comprising; a first portion in a range of 10% to 30% by weight of the mixture of first beads of atomized metallic particles having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 60% to 80% by weight of the mixture of second beads selected from the group consisting of glass, ceramics, alumina, corderite, porcelain and titanates having a specific gravity in the range of 2-3 gr/cm³ and a mesh size in the range of 20-40 and having a third portion in the range of 5% to 15% by weight of the mixture of a partitioning and lubricating particulate material having a specific gravity in the range of 2-3 gr/cm³ and a mesh size in the range of 20-325.
 3. A mixture for balancing a tire comprising; a first portion in a range of 10% to 30% by weight of the mixture of first beads of atomized metallic particles having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 60% to 80% by weight of the mixture of second beads selected from the group consisting of glass, ceramics, alumina, corderite, porcelain and titanates having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40 and having a third portion in the range of 5% to 15% by weight of the mixture of a partitioning and lubricating particulate material having a specific gravity in the range of 2-3 gr/cm³ and a mesh size in the range of 20-325 and having a fourth portion in the range of 1% to 5% by weight of the mixture of a desiccating particulate matter of a mesh size in the range of 20-40.
 4. A mixture for balancing a tire comprising; a first portion in a range of 15% to 30% by weight of the mixture of first beads of atomized metallic micro-spheres having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 70% to 85% of the mixture of second beads of glass having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40.
 5. A mixture for balancing a tire comprising; a first portion in a range of 10% to 30% by weight of the mixture of first beads of atomized metallic micro-spheres having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 60% to 80% by weight of the mixture of second beads of glass having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40 and having a third portion in the range of 5% to 15% by weight of the mixture of vermiculate having a specific gravity in the range of 2-3 gr/cm³ and a mesh size in the range of 20-325.
 6. A mixture for balancing a tire comprising; a first portion in a range of 10% to 30% by weight of the mixture of first beads of atomized metallic micro-spheres having a specific gravity in the range 5-9 gr/cm³ and a mesh size in the range of 80-325; and a second portion in a range of 60% to 80% by weight of the mixture of second beads of glass having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40 and having a third portion in the range of 5% to 15% by weight of the mixture of vermiculate having a specific gravity in the range of 2-3 gr/cm³ and a mesh size in the range of 20-325 and having a fourth portion in the range of 1% to 5% by weight of the mixture of silica gel of a mesh size in the range of 20-40.
 7. A mixture for balancing a truck tire comprising by weight; atomized metallic micro-spheres in the range from 15% to 20% of the mixture having a specific gravity in the range of 5-9 gr/cm³ and having a mesh size in the range of 80-325, glass spheres in the range of 65% to 75% of the mixture having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40, vermiculite in the range of 7% to 12% of the mixture and having a mesh size of 20-325 and a specific gravity of 2-3 gr/cm³, silica gel in the range of 2% to 4% of the mixturehaving a mesh size in the range of 20-40.
 8. A mixture for balancing a truck tire comprising by weight; 17% atomized metal selected from the group consisting of brass, bronze and zinc having a specific gravity in the range of 5-9 gr/cm³ and having a mesh size in the range of 80-325, 70% glass beads of lead-free soda lime glass having a specific gravity in the range of 2-3 gr/cm³ and having a mesh size in the range of 20-40, 10% vermiculite having a specific gravity in the range of 2-3 gr/cm³ and having a mesh size in the range of 20-325 and 3% silica gel having a mesh size in the range of 20-40.
 9. A mixture for balancing a automobile tire comprising atomized metallic micro-spheres in the range of 20% to 30% of the mixture by weight having a specific gravity in the range of 5-9 gr/cm³ and having a mesh size in the range of 80-325 , glass beads in the range of 60% to 70% having a specific gravity in the range of 2-3 gr/cm³ and having a mesh size in the range of 20-40, vermiculite in the range of 5% to 12% having a specific gravity in the range of 2-3 gr/cm³ and having a mesh size in the range of 20-325, silica gel in the range of 1% to 3% having a mesh size in the range of 20-40.
 10. A mixture for balancing a automobile tire comprising by weight; 24% of atomized metallic micro-spheres selected from the group consisting of brass, bronze and zinc having a specific gravity in the range of 5-9 gr/cm³ and having a mesh size in the range of 80-325, 65% of glass beads of lead-free soda lime glass having a specific gravity of 2-3 gr/cm³ and a mesh size in the range of 20-40, 9% of vermiculite having a specific gravity in the range of 2-3 gr/cm³ and having a mesh size in the range of 20-325 and 2% of silica gel having a mesh size in the range of 20-40. 